Features:

  • High abrasion resistance
  • High temperature resistance
  • Non machine able and rough/smooth surface finish
  • Ideal for repair and prevention of surfaces
  • Repair and resurface of worn out surface area
  • Excellent adhesion with metal and concreate surface
  • Protection against abrasive slurry and solid particles
  • Cold casting and bonding of metal to metal, metal to ceramic
  • Longer durable service life span


Applications Area:

  • Apply as erosion resistant coating to protect metal and concreate surface
  • Repairing of ceramic line parts and components
  • Ceramic liner gap filling
  • Development of cold cast parts


Industrial Applications:

  • Pipeline
  • Elbow
  • Bend
  • Slurry line
  • Exhausters
  • Tanks
  • Dredging equipment
  • Blowers
  • Serew conveyers
  • Cyclones
  • Hoppers
  • Chutes mud pumps
  • Slurry valves
  • Repairing of high alumina tiles liners
  • Ball mill liner repairing
  • Feed plates
  • Pan casing
  • Bucket elevators
  • Dust collector
  • Repairing
  • Leak seal and patch work of differnet parts etc
  • Major applications in mining, cement, power, petrochemicals, pulp and paper, fertilizers
Read More...


Details

Properties Compound (JTBC-SL-90) Putty (JPP-SL-90)
Density 3 gram/cc 2.8 gram/cc
Curing time 4 to 6 hours 4 to 6 hours
Mixing ratio 1:1 (Resin:1 hardener) 1:1 (Resin:1 hardener)
Working time 20-30 minutes 45 minutes
Coverage time 13 Kg/1 m2 @ 4-5 mm thick 10-12 Kg/cm2 @ 4-5 mm thick
Machineability Non Machineable Machineable
Shore hardness 90 D 85-90 D
Finished Surface Rough Smooth
Flexural Strength 550 Kg/cm2 550 Kg/cm2
Water Absorption Nil Nil
Application material All metals and concrete All metals and concrete
Compressive strength 90 Kg/cm2 850 Kg/cm2
Application process Trowelable Pasteable
Temperature resistance 150 degree C 150 degree C